The performance of a desiccant-filled polyisobutylene edge sealant for organic electronics is reported. The sealant was applied through a low temperature lamination process using glass substrates and various seal widths. The performance was tested using the Ca corrosion method at 50 degrees C and 80% relative humidity (RH). Data show an effective water vapor transmission rate (WVTR), on the order of 10(-3) g/m(2)/day in the transient regime with a breakthrough time greater than 1400 h for seals 1.5 mm wide and 0.3 mm thick. By changing the sealant architecture, the breakthrough time was increased with similar effective WVTRs. Finally, the sealant was applied to organic electrochromic devices, which displayed a retention of performance after 1000 h of storage at 50 degrees C and 80% RH. (C) 2012 Elsevier B.V. All rights reserved.