Thermochemical storage of solar heat exploits the enthalpy effects of reversible chemical reactions for the storage of solar energy. Among the possible reversible gas solid chemical reactions, utilization of a pair of reduction oxidation (redox) reactions of solid oxides of multivalent metals can be directly coupled to Concentrated Solar Power (CSP) plants employing air as the heat transfer fluid avoiding thus the need for separate heat exchangers. The redox pair of cobalt oxides Co3O4/CoO in particular, is characterized by high reaction enthalpies and thus potential heat storage capacity. Parametric testing of cobalt oxide-based powder compositions via Thermo-Gravimetric Analysis/Differential Scanning Calorimetry was performed to determine the temperature range for cyclic reduction oxidation and optimize the process parameters for maximum reduction and re-oxidation extent. The heating/cooling rate is an important means to control the extent of the oxidation reaction which is slower than reduction. Complete re-oxidation was achieved within reasonable times by performing the two reactions at close temperatures and by controlling the heating/cooling rate. Under proper operating conditions Co3O4 powders exhibited long-term (30 cycles), complete and reproducible cyclic reduction/oxidation performance within the temperature range 800-1000 degrees C. No benefits occurred by using Ni, Mg and Cu cobaltates instead of "pure" Co3O4. The Co3O4 raw material's specific surface area is an influential factor on redox performance to which observed differences among powders from various sources could be attributed. Presence of Na was also shown to affect significantly the evolution of the products' microstructure, though not necessarily combined with improved redox performance. (C) 2014 Elsevier Ltd. All rights reserved.