Amorphous hydrogenated silicon carbide (a-SiC:H) thin films were produced by remote microwave hydrogen plasma chemical vapor deposition (RP-CVD) using dimethylsilane (DMS) and trimethylsilane (TrMS) as single-source precursors. The effect of substrate temperature on the rate of RP-CVD process, chemical composition and chemical structure of resulting a-SiC:H films is reported. The Arrhenius plots of substrate temperature dependencies of the thickness-based film growth rate imply that the investigated RP-CVD for DMS precursor is a non-thermally activated process, whereas for TrMS precursor is an adsorption-controlled process. The examination of the a-SiC:H films performed by means of Auger electron spectroscopy, X-ray photoelectron spectroscopy, and Fourier transform infrared absorption spectroscopy, revealed that the increase in the substrate temperature from 30 degrees C to 400 degrees C causes the elimination of organic moieties from the films and the formation of Si-carbidic network structures. On the basis of the results of structural study the elementary reactions involved in the formation of a-SiC:H films are proposed. (C) 2014 Elsevier B.V. All rights reserved.