Korean Journal of Materials Research, Vol.16, No.6, 373-376, June, 2006
수열합성법에 의한 Ba(Mg1/3Ta2/3)O3 나노분말 합성
Synthesis of Ba(Mg1/3Ta2/3)O3 Nanoparticles by a Hydrothermal Process
E-mail:
[ ] nanoparticles were synthesized in water solution under mild temperature and pressure conditions by precipitation from with aqueous potassium hydroxide. The average size and distribution of the synthesized nanoparticles were below 100 nm and broad, respectively. The phase of synthesized particles was crystalline reacted at for 4 h. The characterization of nanoparticles were studied using XRD, SEM, and TEM.
- Moulson, Herbert, Electroceramics Materials, 55 (2003)
- Matsumoto H, Tamura H, Wakino K, Jpn. J. Appl. Phys., 30(9B), 2347 (1991)
- Wakino K, Tamura H, Ceramic Transition 8., edited by Nair KM etc., p. 305 The American Ceramic Society, Inc. jWesterville, Ohio., (1989) (1989)
- Sugiyama M, Inuzuka T, Kubo H, Ceramic transition 15., edited by Nair KM etc., p.153-166 The American Ceramic Society, Inc. Westerville, Ohio., (1989) (1989)
- Nomura S, Toyama K, Kaneta K, Jpn. J. Appl. Phys., 21(10), L624 (1982)
- Matsumoto K, Hiuga T, Takada K, Ichimura H, Proc. IEEE Int. Symp. Appl. Ferroelectric. 6th, 1118 (1986)
- Galasso FS, Structure, Properties and Preparation of Perovskit-type Compounds., p.13 Pergmon Press (1969) (1969)
- Kawashima S, Nishida M, Ueda I, Ouchi H, J. Am. Ceram. Soc., 66(6), 421 (1983)
- Kim ES, Yoon KH, Ferroelectrics, 133, 187 (1992)
- Lu CH, Tsai CC, J. Materials Lett., 31, 271 (1997)