The injection molded Fe sintered bodies were fabricated using two kinds of Fe powders haying 50 nm and in diameter. In the using of Fe powder having 50 nm in diameter, the comparatively dense bodies () were obtained even at low sintering temperature (), while in the sintered bodies () using Fe powder, their relative densities showed low values about , although they were strongly depend on the sintering temperature and volume ratio of Fe powder and binder. In the sintered bodies using of 50 nm Fe powders, the volume shrinkage and grain size increased as the sintering temperature increased, but the values of hardness decreased. In the sample sintered at , the values of relative density, volume shrinkage and grain size were , respectively and the minimum value of wear depth was obtained due to combination of fine grain and comparatively high density.