유진놀을 이용한 수산화아파타이트 성형체에 관한 연구

류수착; Ryu Su-Chak

Korean Journal of Materials Research, Vol.14, No.6, 375-378, June, 2004

DOI10.3740/MRSK.2004.14.6.375 Export Citation

유진놀을 이용한 수산화아파타이트 성형체에 관한 연구

Study on the Hydroxyapatite Body Using with the Eugenol

류수착^†

밀양대학교

Ryu Su-Chak^†

Dept. of Materials Engineering, Miryang National University, Korea

E-mail:

The samples were prepared with hydroxyapatite(HAp) powder and eugenol (Eugenol/HAp = 15, 20, 25, 30wt%). The samples were dried at room temperature. The higher mechanical properties was observed in HAp sample with 25wt% Eugenol. The average compressive and bending strength in HAp with 25wt% Eugenol are 542 kgf/ mm 2 and 366 kgf/ mm 2 respectively. This strength is higher compare to that of the cortical bone.

Keywords:Hydroxyapatite;Eugenol;Compressive strength;Cortical bone

[References]

Lee DY, Lee SK, Park H, Kim CE, J. Kor. Ceram. Soc., 28(5), 373 (1991)
Ha JW, Jung HJ, J. Kor. Ceram. Soc., 20(1), 55 (1983)
Son YD, Song TW, J. Kor. Ceram. Soc., 36(12), 1342 (1999)
Hench LL, Wilson J, World Scientific, Singapore, New Jersey, London, Hongkong, Ch.1 (1988) (1988)
Legeros RZ, CRC Press, London & Tokyo, 3-28 (1994) (1994)
Smith DK, CRC Press, London & Tokyo, 29-44 (1994) (1994)
Fang Y, Agrawal DK, Roy DW, CRC Press, London & Tokyo, 269-282 (1994) (1994)
Jo SB, Youn YJ, Ceramist, 3(3), 5 (2000)

[1] Lee DY, Lee SK, Park H, Kim CE, J. Kor. Ceram. Soc., 28(5), 373 (1991)

[2] Ha JW, Jung HJ, J. Kor. Ceram. Soc., 20(1), 55 (1983)

[3] Son YD, Song TW, J. Kor. Ceram. Soc., 36(12), 1342 (1999)

[4] Hench LL, Wilson J, World Scientific, Singapore, New Jersey, London, Hongkong, Ch.1 (1988) (1988)

[5] Legeros RZ, CRC Press, London & Tokyo, 3-28 (1994) (1994)

[6] Smith DK, CRC Press, London & Tokyo, 29-44 (1994) (1994)

[7] Fang Y, Agrawal DK, Roy DW, CRC Press, London & Tokyo, 269-282 (1994) (1994)

[8] Jo SB, Youn YJ, Ceramist, 3(3), 5 (2000)