Biaxially oriented polypropylene (BOPP) film is one of the most popularly used materials for the gravure printing process in flexible packaging industry. The skin layers of BOPP film were associated with 3-6 weight % of propylene-ethylene copolymer. These films were completely biaxial-oriented by sequential stretching process after which the film surfaces were subjected to corona treatment integrated in the production line. The FT-IR results exhibited that polar functional groups as carbonyl molecules were established on the corona-treated BOPP film. The contact angles of these BOPP films were measured; the surface free energies (SFE) were then calculated. AFM topographical images also agreed well with the SFE which increased as the contents of propylene-ethylene copolymer increased. An approximated 20% increased SFE was obtained for the BOPP film that was associated with 6% propylene-ethylene copolymer. The printing quality on BOPP films was tested by light microscope which confirmed that the chromatic resolution of the printed images improved down to even more smaller groove sizes, 10 or 5 dot%. This improvement was also examined and found to correspond well with the interfacial tensions and work of adhesion between the inks and the modified BOPP films. (C) 2014 Elsevier B.V. All rights reserved.