CuCr2O4 nanoparticles with cubic-like morphology were prepared via hydrothermal synthesis method without template. The CuCr2O4 samples were characterized by thermogravimetry and differential scanning calorimetry (TG-DSC), X-ray diffraction (XRD), transmission electron microscopy (TEM), X-ray photoelectron spectroscopy (XPS), UV-vis diffuse reflectance spectra (DRS) and Zeta potentials, respectively. The results indicated that cubic-like CuCr2O4 could be successfully synthesized by calcining the precursor at 600 degrees C, and the calcination temperature greatly influenced the morphology and optical performance of CuCr2O4. The pH at the point of zero charge (pH) of the CuCr2O4 calcined at 600 degrees C was about 4.52. The photocatalytic activity of CuCr2O4 was evaluated for degradation of rhodamine B (RhB), methylene blue (MB), and methyl orange (MO) in the presence of H2O2 under visible light irradiation and the effects of the calcination temperature, dosage of photocatalyst, etc., on photocatalytic activity were studied in detail. The photocatalytic results revealed that the CuCr2O4 photocatalyst was of high activity for degradation of RhB (96.8%) and MB (99.5%), but very low activity for degradation of MO (14%). The CuCr2O4 sample calcined at 600 degrees C possesses the best photocatalytic activity, and the optimal dosage of the CuCr2O4 photocatalyst is 0.4 g/L. (C) 2014 Elsevier B.V. All rights reserved.