Adsorption of SO2 onto Jordanian zeolitic tuff (ZT) was examined in this work. ZT samples were characterized by XRD, XRF, BET and TGA analyses. The sorption process was carried out in a fixed bed column at different operating conditions. The unique measuring technique, namely UIC sulfur coulometer, for SO2 measurement was adopted in this work. Uptake of SO2 by ZT was found to increase with increasing temperature up to a temperature of 200 degrees C and then decrease at higher temperatures. It was also found that drying of ZT, by conventional and microwave heating has a considerable effect on SO2 uptake and breakthrough time. Experimental data for adsorption isotherms were obtained and found to follow the BET isotherm model. It was found that the adsorption process is exothermic in nature. Thermal pre-treatment was found to affect the adsorption capacity and breakthrough time of ZT. The maximum adsorption capacity was obtained after thermal pretreatment of ZT at a temperature of 200 degrees C, which could be linked to the effect of heating on the destruction of crystal structure of phillipsite, the crystal refinement of chabazite, and the formation of new aluminosilicate crystalline phases. ZT can be regenerated and the initial adsorption capacity was preserved after three regeneration cycles. (C) 2014 Elsevier B.V. All rights reserved.