A novel heterometallic oxalate-based compound of the formula {[Co(bpy)(3)][Mn-2(C2O4)(3)].H2O}(n) (1; bpy = 2,2'-bipyridine) was synthesized and characterized by elemental analysis, IR spectroscopy, single-crystal X-ray diffraction (XRD), and magnetization measurement. The molecular structure of 1 is made of a three-dimensional (3D) anionic network, [Mn-2(C2O4)(3)](n)(2n-), and tris-chelated cations [Co(bpy)(3)](2+) occupying the vacancies of the framework. Splitting between the zero-field-cooled (ZFC) and field-cooled (FC) branches of susceptibility below the small peak at 13 K indicates magnetic ordering. Compound 1 was used as a single-source precursor for the formation of the mixed-metal oxide CoMn(2)O4. This conversion via thermal decomposition was explored by thermal analysis (TGA and DTA), IR spectroscopy, powder XRD, and magnetic susceptibility measurement. From refined structural parameters, it could be seen that the spinel obtained by the thermal treatment of 1 at 800 degrees C is characterized by the inversion parameter delta = 21%, and therefore the structural formula at room temperature can be written as (tet)[Co0.79Mn0.21](oct)[Co0.105Mn0.895](2)O-4. The temperature dependence of magnetization for CoMn2O4 points to at least three magnetic phases: the ferrimagnetic state is observed below 83 K, and up to 180 K blocking of the magnetic moments of nanocrystallites of 31 nm appears, transforming to paramagnetic-like behavior above 180 K. Microstructural characterization of the CoMn2O4 sample was carried out by means of XRD line-broadening analysis.