Near-monodisperse, micrometer-sized polypyrrole-palladium (PPy-Pd) nanocomposite-coated polystyrene (PS) particles have been coated with Ni overlayers by electroless plating in aqueous media. Good control of the Ni loading was achieved for 1.0 mu m diameter PPy-Pd nanocomposite-coated PS particles and particles of up to 20 mu m in diameter could also be efficiently coated with the Ni. Laser diffraction particle size analysis studies of dilute aqueous suspensions indicated that an additional water-soluble colloidal stabilizer, poly(N-vinyl pyrrolidone), in the electroless plating reaction media was crucial to obtain colloidally stable Ni-coated composite particles. Elemental microanalysis indicated that the Ni loading could be controlled between 61 and 78 wt% for the 1.0 mu m-sized particles. Scanning/transmission electron microscopy studies revealed that the particle surface had a flaked morphology after Ni coating. Spherical capsules were obtained after extraction of the PS component from the Ni-coated composite particles, which indicated that the shell became rigid after Ni coating. X-ray diffraction confirmed the production of elemental Ni and X-ray photoelectron spectroscopy studies indicated the existence of elemental Ni on the surface of the composite particles. (C) 2014 Elsevier Inc. All rights reserved.