The effects of depositing ultrathin (<1 nm) Al2O3 coatings on LiNi0.5Mn1.5O4 (LNMO) particles using atomic layer deposition (ALD) are presented. Promising electrochemical performance of the Al2O3 ALD coated LNMO at 30 degrees C is demonstrated in not only significantly improved coulombic efficiency, cycle retention, and rate capability, but also in dramatically suppressed self-discharge and dissolution of transition metals. Combined analyses by electrochemical impedance spectroscopy, ex-situ X-ray photoelectron spectroscopy, and ex-situ time-of-flight secondary ion mass spectrometry reveal that the solid electrolyte interphase layer on the Al2O3 ALD coated LNMO is much thinner and contains fewer organic species than the one on the bare LNMO. This difference originates from the suppression of the side reaction at high voltage by the Al2O3 ALD protective coating. Also, fluorination of Al2O3 ALD layer upon repeated charge discharge cycling is confirmed, and this can account for the capacity increases during the initial charge discharge cycles. Finally, it is also demonstrated that a full LNMO/Li4Ti5O12 battery incorporating the Al2O3 ALD coated LNMO outperforms the one incorporating only bare LNMO. (C) 2014 Elsevier B.V. All rights reserved.