Controlling the materials chemistry of the solid-state ion conductor NaSICON is key to realizing its potential utility in emerging sodium-based battery technologies. We describe here the influence of excess sodium on phase evolution of sol-gel synthesized NaSICON. Alkoxide-based sol-gel processing was used to produce powders of Na3Zr2PSi2O12 NaSICON with 0-2 atomic % excess sodium. Phase formation and component volatility were studied as a function of temperature. NaSICON synthesis at temperatures between 900-1100 degrees C with up to 2% excess sodium significantly reduced the presence of zirconia, sodium phosphate, and sodium silicate secondary phases in fired NaSICON powders. Insights into the role of sodium on the phase chemistry of sol-gel processed NaSICON may inform key improvements in NaSICON development.