Stable, multidimensional, and extra-large pore zeolites are desirable by industry for catalysis and separation of bulky molecules. Here we report EMM-23, the first stable, three-dimensional extra-large pore aluminosilicate zeolite. The structure of EMM-23 was determined from submicron-sized crystals by combining electron crystallography, solid-state nuclear magnetic resonance (NMR), and powder X-ray diffraction. The framework contains highly unusual trilobe-shaped pores that are bound by 21-24 tetrahedral atoms. These extra-large pores are intersected perpendicularly by a two-dimensional 10-ring channel system. Unlike most ideal zeolite frameworks that have tetrahedral sites with four next-nearest tetrahedral neighbors (Q(4) species), this unusual zeolite possesses a high density of Q(2) and Q(3) silicon species. It is the first zeolite prepared directly with Q(2) species that are intrinsic to the framework. EMM-23 is stable after calcination at 540 degrees C. The formation of this highly interrupted structure is facilitated by the high density of extra framework positive charge introduced by the dicationic structure directing agent.