This research focused on photodegradation of organic compound by a fixed bed photoreactor. The photoreactor consists of a cylindrical glass tube, was filled by TiO2 coated glass beads codoped with sulfur and nitrogen (S, N). The photoactive layer of TiO2 was deposited on glass beads using the sol gel dip-coating technique. The S, N-codoped TiO2 film after thermal treatment at 500 degrees C for 1 h, was characterized by XRD, XPS, SEM and EDX analyses. The XRD analyses exhibited an anatase structure of TiO2 with particle size about 35 rim. The photocatalytic activity was determined by degradation of methyl orange (MO) (7 mg/L, pH 2). The effective parameters of photocatalyst efficiency were investigated in laboratory and large volume scales under visible and sun light irradiations. The results showed that visible-light photocatalytic activity of TiO2 was extremely increased through adding thiourea (Tu) as a source of nitrogen and sulfur into TiO2 sol, which conducted to degradation of MO solution up to 95% in sunlight irradiation after only 2 h. Overall, the photoreactor of immobilized S, N-codoped TiO2 on glass beads was found to be a promising technology for water treatment. (C) 2014 Elsevier Ltd. All rights reserved.