A facile, self-reduction and size controlled synthesis method has been explored to fabricate silver nanoparticles (Ag NPs) on carbon nanosphere (CNs) under mild conditions. Without using predeposition of seed metals and reducing agent, a uniform and complete layer of Ag NPs was formed through grafting a molecular layer on CNs surfaces under UV irradiation. The size and thickness of Ag NPs were effectively tuned by adjusting the UV irradiation time. This direct formation of Ag NPs was attributed to self seed in aqueous Ag(NH3)(2)(+) complex solution through a triazine-based silane coupling agent molecular layer, even at 25 degrees C. Scanning electron microscopy (SEM), Transmission electron microscope (TEM), and X-ray photoelectron spectroscopy (XPS) were employed to characterize the Ag NPs' properties. A substantial conductivity improvement of prepared Ag NPs on carbon nanosphere was demonstrated. The presented method is simple and environmentally friendly and thus should be of significant value for the industrial fabrication of Ag NPs on carbon nanosphere in conduct electricity paint and coating applications. (C) 2015 Elsevier B.V. All rights reserved.