In contrast to convex nano-pattern sapphire substrates (NPSS), which are frequently used to fabricate high-quality nitride-based light-emitting diodes (LEDs), concave NPSS have been paid relatively less attention. In this study, a concave NPSS was fabricated, and its nitride epitaxial growth process was evaluated in a step by step manner. A SiO2 layer was used to avoid nucleation over the sidewall and bottom of the nano-patterns to reduce dislocation reformation. Traditional LED structures were grown on the NPSS layer to determine its influence on device performance. X-ray diffraction, etched pit density, inverse leakage current, and internal quantum efficiency (IQE) results showed that dislocations and non-radiative recombination centers are reduced by the NPSS constructed with a SiO2 blocking layer. An IQE twice that on a planar substrate was also achieved; such a high IQE significantly enhanced the external quantum efficiency of the resultant device. Taken together, the results demonstrate that the SiO2 blocking layer proposed in this work can enhance the performance of LEDs. (C) 2015 Elsevier B.V. All rights reserved.