Gold nanoparticles are prepared in various concentrations of NaCl solutions by solution plasma sputtering. The absorption spectra of these solutions during and after the plasma process are measured by in situ ultraviolet-visible (UV-vis) spectroscopy to estimate the particle diameters and concentrations of gold. The distributions of particle diameters are obtained by transmission electron microscope (TEM) observations. These experiments indicate the gold nanoparticles with about 2.2 nm are directly formed by plasma phase and the diameters are increasing over time. These increases of particle diameters are caused by Ostwald ripening of gold nanoparticles in NaCl solution. We estimate the equilibrium diameter at which the gold nanoparticles are not solved in NaCl solution using in situ UV-vis spectroscopy. These diameters are about 5, 7 and 10 nm in 3, 5 and 10 mM NaCl solution, respectively. We make it possible to control the diameter of gold nanoparticles prepared by solution plasma sputtering in NaCl solution. (C) 2015 Elsevier B.V. All rights reserved.