Monometallic noble metal catalysts supported on ceria-zirconia mixed oxide were prepared by impregnation and tested in the oxidation of chlorobenzene (100 ppm in air). With the pure ceria-zirconia support, 27% conversion was achieved at 400 degrees C and only incomplete oxidation to carbon monoxide was evidenced. The introduction of gold and especially platinum significantly improved the efficiency of the catalyst. The catalytic performance increased with increasing noble metal content. The catalyst with 1 wt.% of Pt achieved 97% conversion of chlorobenzene already at 350 degrees C and complete oxidation to CO2 with only traces of by-products was detected. Platinum catalysts were more efficient than gold ones, which was ascribed to their superior redox properties. On the other hand, the lower acidity of platinum catalysts was not detrimental for their catalytic performance. (C) 2015 Elsevier B.V. All rights reserved.