Zeolitic imidazolate framework-8 (ZIF-8) membrane has shown great potential for propylene/propane separation based on molecular sieving mechanism. Although diverse synthesis strategies were applied to prepare ZIF-8 membranes, it is still a challenge for reproducible fabrication of high-quality membranes. In this study, high-quality ZIF-8 membranes were prepared through hydrothermal synthesis under the partial self-conversion of sputter-coated ZnO layer on porous alpha-alumina supports. The reproducibility was significantly improved, compared with that from sol-gel coated ZnO layer, due to the highly controllable sputtering deposition of ZnO precursor. The relationship between the quality of as-synthesized membrane and amount of deposited ZnO was also determined. The effect of pressure drop in C3H6/C3H8 separation on separating performance was also examined. (C) 2015 Elsevier Ltd. All rights reserved.