Electrochimica Acta, Vol.184, 403-409, 2015
Prevention of Reaction between (Ba,Sr)(Co,Fe)O-3 Cathodes and Yttria-stabilized Zirconica Electrolytes for Intermediate-temperature Solid Oxide Fuel Cells
Perovskite (Ba,Sr)(Co,Fe)O-3 (BSCF) cathodes are highly electrochemically active in the oxygen reduction process for intermediate-temperature solid oxide fuel cells (IT-SOFCs). However, the phase of perovskite zirconate is formed between the BSCF cathode and yttria-stabilized zirconia (YSZ) electrolyte, which increased the cathode polarization resistance. In the present work, the (Ba, Sr)ZrO3 formation was not prevented by the insertion of a porous gadolinia-doped ceria (GDC) interlayer between the cathode and the electrolyte, when the BSCF cathode was sintered at 1100 degrees C. Energy dispersive X-ray spectroscopy showed that the product of (Ba, Sr)ZrO3 formed between BSCF and YSZ was thicker than that of SrZrO3 formed between a conventional (La, Sr)(Co, Fe)O-3 (LSCF) and YSZ. When a BSCF cathode was sintered at 900 degrees C, no (Ba,Sr)ZrO3 formation was observed between the cathode and the electrolyte. The maximum power density at 650 degrees C was improved from 7.5 to 740 mW/cm(2) by decreasing the sintering temperature of BSCF cathode from 1100 degrees C to 900 degrees C. Distribution of relaxation times (DRT) analysis showed that the polarization resistance of the oxygen exchange process in the BSCF cathode sintered at 900 degrees C was lower than that in the LSCF cathode. The sintering temperature is important for obtaining high-performance BSCF cathodes for IT-SOFCs. (C) 2015 Elsevier Ltd. All rights reserved.
Keywords:intermediate-temperature solid oxide fuel cell (IT-SOFC);cathode;perovskite oxide;mixed ionic and electronic conductor (MIEC)