Mechanism of CWS (coal water slurry) electrolysis was investigated by using anode reaction kinetics. The results indicated that the activation energies of electrode reaction reduce with the increase in activity of carbon materials. According to the electrode reaction kinetics, the direct oxidation of CWS electrolysis occurred easily under lower concentration of electrolyte and higher concentration of CWS. On the contrary, the indirect oxidation of CWS electrolysis took place. Because of the high oxygen evolution potential of water electrolysis in H2SO4 solution (1.23 V), the direct oxidation of CWS electrolysis mainly occurred under water decomposition potential (0.5-1.23 V). As NaOH solution was used as electrolyte, it was difficult to distinguish direct and indirect oxidation under the low potential (0.4 V). With increasing stirring rate, the electrode reaction activation energies of GWS (graphite water slurry) electrolysis increased slightly and were always lower than 40 kJ/mol. The results indicated that GWS electrolysis was controlled by diffusion and the increase in stirring rate could not reduce the polarization. (C) 2015 Elsevier Ltd. All rights reserved.