This paper presents the experimental investigation on the thermal properties and electrical conductivity of the new microencapsulated phase change material by entrapping of stearic acid (SA) into PANI (polyaniline) shell through self-assembly method. Experimental results reveal that PANI nuclei grew on the surface of SA, and then copied its original morphological structure and finally exhibited peony flower-like morphology. The two components have good compatibility and have no chemical reaction both in the process of fabrication and subsequent use, while hydrogen bondings between the imino groups and carboxyl groups exist. The maximum mass fraction of stearic acid loaded in SA/PANI is determined as high as 62.1 wt% without seepage of melted SA from capsules. Due to the secondary doping with carboxyl group, the composite phase change material embedded with SA exhibits improved electrical conductivity from 0.3968 S cm(-1) to 0.7042 S cm(-1) when compared to PANI. The phase change temperatures and latent heats of SA/PANI are measured to be 55.6 degrees C and 113.02 J/g for melting and, 50.8 degrees C and 112.58 J/g for freezing, respectively. TG analysis test revealed that the prepared SA/PANI composite PCM has high thermal durability in working temperature range. Moreover, the results of DSC, FT-IR, TG, conductivity investigation and thermal cycling test are all show that the thermal reliability and electrical conductivity of the SA/APNI have imperceptible changes. In total, the additional electrical conductivity, high heat storage potential and good thermal reliability and stability facilitated SA/PANI to be considered as a viable candidate for thermal energy storage, antistatic thermo-regulating textiles and other applications. (C) 2015 Elsevier Ltd. All rights reserved.