Investigation of the compaction of unidirectionally arranged high-tenacity polypropylene fibres is described. A combination of techniques, with the major emphasis being morphological studies, show that controllable "selective" surface melting is not achieved at a high enough proportion to give substantial fibre-to-fibre bonding, and hence good lateral strengths.