Phases in equilibrium with the alpha Zr solid solution from 1014-1314 degrees C (1287-1587 K) in zirconium-tin-oxygen alloys were characterized and their compositions were determined. The experimental results provide information on the equilibria of the alpha Zr solid solution in order to propose tentative boundaries at isothermal sections of the phase diagram.