Aqueous solutions of xAl(NO3)(3)+(1-x)ZrO(NO3)(2) were used for electrodeposition of ceramic Al2O3-ZrO2 composite coatings on TiC, TiB2 and SiC substrates. The weight of the deposit was studied versus the duration of deposition, the current density and the temperature of the bath for Al-rich (x=0.9), Zr-rich (x=0.4) and eutectic (x=0.75) electrolyte compositions. Optimal current densities and durations of deposition were determined to obtain maxima weights of deposits. Amorphous deposits with thicknesses up to 10 mu m were formed. The microstructure and microchemical composition of the as-deposited and sintered deposits were characterized. Increase in the temperature of the bath inhibited microcracking due to shrinkage during drying. Coated TIC substrates exhibited enhanced oxidation resistance in air at 1100 degrees.