Pt-FeOx-CeO2 catalysts for the preferential oxidation of CO (CO-PROX) with controllable segregation between the Pt/FeOx and CeO2 components were synthesized by two-nozzle flame spray pyrolysis. This was achieved by flame-spraying the two active components independently in two interfacing flames. By adjusting the intersection distance between the two aerosol flames, it was possible to tune the morphology and the reducibility of the catalysts. Intimate interactions between Pt/FeOx and CeO2 (without oversintering the two components) achieved at the greatest flame distance gave reducibility at the lowest temperature, as corresponding to the formation of oxygen vacancies around the Pt (from H-spillover). Maximum CO conversion (>99.5%) for the two-nozzle synthesized catalysts was achieved below 90 degrees C, which is 30 degrees C lower than for mechanically mixed Pt/FeOx and CeO2. While high CO2 selectivity was attained at lower temperatures, it was limited by the adsorption of reactive oxygen. The oxygen vacancies on the Pt-FeOx-CeO2 catalyst were gradually oxidized at low temperatures due to unconsumed O-2, and this led to a decrease in CO conversion with time on stream. In contrast, complete consumption of O-2 and excess of dissociated H-2 sustained the high oxygen vacancies content at high temperatures and hence high activity (although nonselective) was achieved. We further identified the loss of CO2 selectivity at high temperature as originating from the weakened CO adsorption compared to that of H-2 in the presence of oxygen vacancies. (C) 2015 Elsevier Inc. All rights reserved.