One-dimensional (1D) magnetic Fe3O4/P(MBAAm-co-MAA) nanochains were prepared by distillation-pre cipitation polymerization of MBAAm and MAA in the presence of Fe3O4 nanoparticles as building blocks under a magnetic heating stirrer, which played two critical roles: serving as magnetic field to induce the self-assembly of Fe3O4 nanoparticles into 1D nanochains and providing thermal energy to induce the polymerization of MAA and MBAAm on the surface of the Fe3O4 nanoparticles. The thickness of the P(MBAAm-co-MAA) layer can be easily tuned by adjusting the successive polymerization steps. The polymer layer that contained carboxyl groups was used as stabilizers for loading Ag nanoparticles and the reaction locus for deposition of outer silica layer via a sol-gel method in presence of C18TMS as the pore directing agent for tri-layer nanochains. The corresponding hollow mesoporous silica nanochains with movable maghemite cores (gamma-Fe2O3@mSiO(2)) were produced after removal of the polymer mid-layer and the alkyl groups of the pore directing agent via calcination of the tri-layer nanochains at high temperature. The Fe3O4/P(MBAAm-co-MAA)/Ag nanochains exhibited a highly catalytic efficiency and well reusable property toward the reduction of nitrophenol. Furthermore, the gamma-Fe2O3@mSiO(2) nanochains possessed hollow mesoporous structure and high specific surface area (197.2 m(2) g(-1)) were used as a drug carrier, which displayed a controlled release property. (C) 2015 Elsevier Inc. All rights reserved.