Ag and Ag-based pseudo-alloys were evaluated in terms of application as metal brazes for the use in a hybrid direct carbon fuel cell stack. This paper reports on a series of wetting experiments on systems of pure Ag as well as Ag-Cu-Ti and Ag-Cu-Ni pseudo-alloys in contact with the widely used austenitic stainless steel SS316L, the ferritic steels Crofer22APU and Croffer22H and with polycrystalline partially stabilized zirconia (TZ-3Y) for the determination of the interfacial properties of the above systems. Pure Ag in air showed poor wettability (theta > 90A degrees) with all substrates. The Ag-Cu-Ti pseudo-alloy in vacuum (P = 2.5 x 10(-3) mbar) showed improved wettability, with theta a parts per thousand 40A degrees for the steels and theta a parts per thousand 50A degrees for the TZ-3Y substrates. The Ag-Cu-Ni pseudo-alloy in air showed excellent wetting properties (theta < 10A degrees) with all the substrates, but its high liquidus temperature makes it unsuitable for use with the SS316L steel. In low vacuum (P = 1.5 x 10(-1) mbar), the contact angle was increased (theta a parts per thousand 65A degrees) but the low oxygen concentration limits the oxidation of the steel surface. Selected systems of the pseudo-alloys in contact with steel and TZ-3Y substrates were treated for 120 h in the operating conditions of a hybrid direct carbon fuel cell, in order to evaluate the thermal stability of the joints. Despite the reactions taking place on the interface, the joints showed good stability and no separation of the two phases occurred.