Recent studies have suggested that impact-induced devitrification of fused silica, or more specifically formation of high-density stishovite, can significantly improve ballistic-penetration resistance of fused silica, the material which is used in transparent armor. The studies have also shown that in order for stishovite to form during a ballistic-impact event, very high projectile kinetic energy normalized by the projectile/fused-silica target-plate contact area must accompany such an event. Otherwise fused-silica devitrification, if taking place, does not substantially improve the material ballistic-penetration resistance. In the present work, all-atom molecular-level computations are carried out in order to establish if pre-shocking of fused-silica target-plates (to form stishovite) and subsequent unloading (to revert stishovite to the material amorphous structure) can increase fused silica's propensity for stishovite formation during a ballistic impact. Towards that end, molecular-level computational procedures are developed to simulate both the pre-shocking treatment of the fused-silica target-plate and its subsequent impact by a solid right-circular cylindrical projectile. The results obtained clearly revealed that when strong-enough shockwaves are used in the fused-silica target-plate pre-shocking procedure, the propensity of fused silica for stishovite formation during the subsequent ballistic impact is increased, as is the associated ballistic-penetration resistance. To rationalize these findings, a detailed post-processing microstructural analysis of the pre-shocked material is employed. The results obtained suggest that fused silica pre-shocked with shockwaves of sufficient strength retain some memory/embryos of stishovite, and these embryos facilitate stishovite formation during the subsequent ballistic impact.