Journal of Materials Science, Vol.33, No.15, 3875-3884, 1998
Early fatigue damage in carbon-fibre composites observed by electrical resistance measurement
Early fatigue damage during the first tenth (or less) of the fatigue life was observed in carbon fibre composites by d.c. electrical resistance measurement. The damage was most severe in the first loading cycle and the incremental damage in each subsequent cycle diminished cycle by cycle. For the continuous carbon fibre carbon-matrix composite, the resistance increased irreversibly du ring early fatigue due, to matrix damage and possibly fibre fracture as well. For the short carbon fibre polymer-matrix and cement-matrix composities, the resistance decreased irreversibly during early fatigue due to matrix damage near the junction of adjacent fibres and the resulting increase in the chance that adjacent fibres touched one another.