The condensation of water vapor on a volatile polymeric solution leads to a porous surface after evaporation of both solvent and water. However, the stabilization of the water microdroplet is of great importance, which can be achieved using specific polymer or adding a third substance to the polymer solution. Short chain alcohols (methanol, ethanol, and n-propanol) are utilized to fabricate a self-assembled porous honeycomb film of linear, low molecular weight polystyrene using the breath figure technique. A combination of breath figure processing and the effect of alcohol on a water droplet can stabilize the pattern and make pores on the surface of the polymer film. The quality of the porous honeycomb film is strongly dependent on the type of alcohols and the concentration of polymer. In a specific range of polymer and alcohol concentration, pores cover all the surface of the polymer film. This method offers the possibility of producing a honeycomb structure with no trace of additive residual after the fabrication process and avoiding polymer modification. (c) 2015 Wiley Periodicals, Inc. J. Polym. Sci., Part B: Polym. Phys. 2015, 53, 709-718