Highly active Al-doped CuMnOx catalyst supported on metallic copper foam was prepared via the combustion method and placed adjacent to the anode electrocatalyst of a high temperature PEM fuel cell operating at 200-210 degrees C. The addition of aluminum oxide in the catalyst composition enhanced the specific surface area (19.1 vs. 8.6 m(2) g(-1)) and the reducibility of the Cu-Mn spinel oxide. Accordingly, the catalytic performance of CuMnOx was also improved. The doped sample is up to 2.5 times more active than the undoped sample at 200 degrees C, depending on the methanol concentration at the inlet, while CO selectivity is less than 0.8% in all cases. A membrane-electrode assembly comprising the ADVENT crosslinked TPS (R) high-temperature polymer electrolyte was integrated with the Cu-based methanol reformer in an Internal Reforming Methanol Fuel Cell (IRMFC). In order to avoid extensive poisoning of the reforming catalyst by H3PO4, a thin separation plate was placed between the reforming catalyst and the electrooxidation catalyst. Preliminary results obtained from a single-cell laboratory prototype demonstrated the improved functionality of the unit. Indeed, promising electrochemical performance was obtained during the first 24 h, during which the required H-2 for achieving 580 mV at 0.2 A cm(-2), was supplied from the reformer. (C) 2015 Elsevier B.V. All rights reserved.