ZnFe2O4 nano particles as an anode material for lithium ion batteries are prepared by the glycine-nitrate combustion method. The mixture of styrene butadiene rubber and sodium carboxyl methyl cellulose (SBR/CMC) with the weight ratio of 1:1 is used as the binder for ZnFe2O4 electrode. Compared with the conventional polyvinylidene-fluoride (PVDF) binder, the SBR/CMC binder is much cheaper and environment benign. More significantly, this water soluble binder significantly improves the rate capability and cycle stability of ZnFe2O4. A discharge capacity of 873.8 mAh g(-1) is obtained after 100 cycles at the 0.1C rate, with a very little capacity fading rate of 0.06% per cycle. Studies show that the SBR/CMC binder enhances the adhesion of the electrode film to the current collector, and constructs an effective three-dimensional network for electrons transport. In addition, the SBR/CMC binder helps to form a uniform SEI film thus prohibiting the formation of lithium dendrite. Electrochemical impedance spectroscopy shows that the SBR/CMC binder lowers the ohmic resistance of the electrode, depresses the formation of SEI film and, facilitates the charge transfer reactions at the electrode/electrolyte interface. These advantages highlight the potential applications of SBR/CMC binder in lithium ion batteries. (C) 2015 Elsevier B.V. All rights reserved.