Palladium-ruthenium nanoparticles supported on carbon PdxRu1-x/C (x = 1, 0.99, 0.95, 0.90, 0.80, 0.50) were prepared using a polyol method for ethanol electrooxidation in alkaline media. The resulting bimetallic catalysts were found to be primarily a mix of Pd metal, Ru oxides and Pd oxides. Their electrocatalytic activity towards ethanol oxidation reaction (EOR) in 1M KOH was studied using cyclic voltammetry and chronoamperometry techniques. Addition of 1-10 at.% Ru to Pd not only lowers the onset oxidation potential for EOR but also produces higher current densities at lower potentials compared to Pd by itself. Thus, Pd90Ru10/C and Pd99Ru1/C provide the current densities of up to six times those of Pd/C at -0.96 V and -0.67 V vs MSE, respectively. The current density at different potentials was found to be dependent on the surface composition of PdxRu1-x/C nanostructures. Pd90Ru10/C catalyst with more surface oxides was found to be active at lower potential compared to Pd99Ru1/C with less surface oxides, which is active at higher potentials. The steady-state current densities of the two best catalysts, Pd90Ru10/C and Pd99Ru1/C, showed minimal surface deactivation from EOR intermediates/products during chronoamperometry. (C) 2015 Elsevier B.V. All rights reserved.