Bifunctional and highly uniform Ln:BaGdF5 (Ln = Eu3+ and Nd3+) nanoparticles have been successfully synthesized using a solvothermal method consisting of the aging at 120 degrees C of a glycerol solution containing the corresponding Lanthanide acetylacetonates and butylmethylimidazolium tetrafluoroborate. The absence of any surfactant in the synthesis process rendered hydrophilic nanospheres (with tunable diameter from 45 nm 85 nm, depending on the cations concentration of the starting solution) which are suitable for bioapplications. The particles are bifunctional because they showed both optical and magnetic properties due to the presence of the optically active lanthanides (Eu3+ in the visible and Nd3+ in the NIR regions of the electromagnetic spectrum) and the paramagnetic gadolinium ion, respectively. The luminescence decay curves of the nanospheres doped with different amounts of Eu3+ and Nd3+ have been recorded in order to determine the optimum dopant concentration in each case, which turned out to be 5% Eu3+ and 0.5% Nd3+. Likewise, proton relaxation times were measured at 1.5 T in water suspensions of the optimum particles found in the luminescence study. The values obtained suggested that both kinds of particles could be used as positive contrast agents for MRI. Finally, it was demonstrated that both the 5% Eu3+ and 0.5% Nd3+-doped BaGdF5 nanospheres showed negligible cytotoxicity for VERO cells for concentrations up to 0.25 mg mL(-1).