Superhydrophobic coating system was developed with colloidal silica and crosslinkable fluorocopolymer as filler and matrix respectively, to yield low surface energy and chemical stability, high hardness, and strong adhesion with substrates. The effects of particle surface functionalities, volume fraction and dimension on hydrophobicity and integrity of coatings were systematically investigated. The coating performance was closely dependent on these three factors. Superhydrophobicity (water contact angle similar to 155 degrees and rolling angle similar to 1 degrees) and desired integrity was observed in the coatings with fluorinated particles (with dimension of either 340 or 1450 nm) at optimal particle volume fraction of 60%. (C) 2016 Elsevier Ltd. All rights reserved.