Mesoporous magnesium oxide (MgO) material was synthesized using an integration of the evaporation-induced surfactant assembly and magnesium nitrate pyrolysis. The as-prepared MgO material is well crystalline, and possesses three-dimensional interconnected mesopores and a surface area as high as 596 m(2)/g. Using the porous MgO as a matrix and polyethylene glycol (PEG-1000) as the functional phase for heat energy storage, a shape-stabilized phase change composite of PEG/MgO was fabricated by an easy impregnation method. In the composite, mesoporous MgO material provides structural strength and prevents the leakage of the molten PEG during the phase change process. The compositions and microstructures of the PEG/MgO composite were determined by Fourier transformation infrared spectroscope (FT-IR), X-ray diffractometer (XRD), scanning electronic microscope (SEM) and thermogravimetric analyzer (TGA), respectively. The phase change properties of the PEG/MgO composite were deterthined by differential scanning calorimeter (DSC). The high heat-energy storage capability and good thermal stability of the composite enable it extensive applications in the future. (C) 2015 Elsevier B.V. All rights reserved.