Tin(II) sulfide (SnS) films are one of the most promising absorber materials for high efficiency solar cells without using rare metals. In this work, SnS films were deposited by the thermal evaporation on glass substrates under the variation of growth temperatures of 100-250 degrees C. It was revealed that the SnS thin film prepared under the temperature of 100 degrees C had relatively small crystal grains. On the other hand, the denser and larger crystal grains of the SnS films were obtained with the constant compositions, when the growth temperature increased to 225 degrees C. With the temperature of higher than 225 degrees C, the SnS began to be re-evaporated from the films. The highest Hall mobility of the films was obtained under the temperature of 200 degrees C. Ultimately, the results suggested that the optimized growth temperature of SnS by the evaporation is 200 degrees C, giving rise to compact and large crystal grains and the highest Hall mobility, thereby contributing to the 2.53%-efficient SnS thin-film solar cell. (C) 2015 Elsevier B.V. All rights reserved.