Powder mixtures of MgB2 and B4C with composition ((MgB2) + (B4C) x, x = 0.005, 0.01, 0.03) were consolidated by Spark Plasma Sintering at 1150 degrees C for 3 min. The average particle size of B4C raw powder was relatively high of 4 mm. Despite this, it is shown that processing processes are fast and, as in the case of the in-situ routes, for our ex-situ method carbon substitutes for the boron in the crystal lattice of MgB2. Specifics of microstructure are discussed based on electron microscopy observations. Carbon substitution and microstructure contribute to enhancement of the critical current density J(c) at high magnetic fields and of the irreversibility field H-irr. Samples are shown to be in the point pinning limit with some tendency toward the grain boundary pinning depending on B4C doping amount and temperature. An optimum composition is found for x = 0.01: for this sample, at 20 K, a J(c) of 100 A/cm(2) is obtained at 5.35 T. This value is higher than for the pristine MgB2 sample and for an optimum ex-situ nano-SiC-doped sample obtained for the same SPS processing conditions. (C) 2015 Elsevier B.V. All rights reserved.