복합기능(대전방지/미끄럼 방지)을 보유한 열경화형 코팅제의 합성 및 그 응용에 관한 연구
A Study on the Polymerization and Application of Thermally Curable Multi-Functional (Anti-Static/Slip-Stop) Coating Composition
The thermally curable coating composition with anti-static (AS-2001) and slip-stop (SㆍS) fuctions was synthesized. The multi-functional coating agents formulated with AS-2001 and SㆍS with water-born polyurethane. The additive amounts of multi-functional coating agent are varied from 5 to 12 wt% depending on the amount of polyurethane used. The optimum amount of coating agent was 10 wt%. The ratio of coating composition "AS-2001:SㆍS" was 8:2. The surface electric resistance and friction factor of coated layer were 10(9)Ω/cm(2) and 0.88 respectively in optimum condition.