Journal of the Electrochemical Society, Vol.163, No.6, F523-F532, 2016
Application of the Adler-Lane-Steele Model to Porous La2NiO4+delta SOFC Cathode: Influence of Interfaces with Gadolinia Doped Ceria
Electrochemical impedance spectroscopy measurements carried out on La2NiO4+delta(LNO)//Ce0.8Gd0.2O2-delta(GDC)//3mol.% Y2O3-ZrO2(TZ3Y) half-cells from 500 degrees C to 800 degrees C revealed that the impedance of the LNO electrode is Gerischer-like. Based on experimental data of the porosity, tortuosity, surface area, molar volume and thermodynamic factor of the LNO electrode sintered at 1200 degrees C, the ionic conductivity si(LNO) and the surface exchange coefficient R-0 of the LNO electrode are calculated using the Adler-Lane-Steele (ALS) model. Surprisingly, the polarization resistance of the half-cell is shown to depend on the sintering temperature of the GDC interlayer, which is varied from 1200 degrees C up to 1450 degrees C. Whatever the sintering conditions of GDC, the calculated R-0 values agree with those obtained by recently published pulse isotopic exchange (PIE) experiments. Indeed, the oxygen reduction reaction mostly occurs at the LNO grain surface. However, the calculated ionic conductivity of the electrode vary depending on the GDC sintering temperature. X-ray diffraction studies of the LNO//GDC and GDC//TZ3Y interfaces reveal that cations interdiffusion occurs in both cases. The interfacial GDC layer may act as a bottleneck for the oxide ion transfer from the LNO electrode toward the TZ3Y electrolyte, and vice-versa, resulting in an increase of the series and polarization resistances. (C) 2016 The Electrochemical Society.