Porous poly(benzimidazole) (PBI) membranes of low vanadium ions permeability are described for an all vanadium redox flow battery (VRFB). The PBI membrane was prepared by a water vapour induced phase inversion process of a PBI polymer solution. The membrane has a symmetrical cross-sectional morphology. A low water permeability of 16.5 L (m(2) h bar)(-1) indicates the high hydraulic resistance stemming from a closed cell morphology with nanoporous characteristics. The PBI membrane doped with 2.5 M H2SO4 shows a proton conductivity of 16.6 mS cm(-1) and VO2+ permeability as low as 4.5 x 10(-8) cm(2) min(-1). The stability test of dense PBI membrane in VO2+ solution indicates good chemical stability. An all vanadium redox flow battery (VRFB) operated with the porous PBI membrane shows 98% coulombic efficiency and more than 10% higher energy efficiency compared to VRFB operated with Nafion 112 at applied current densities of 20-40 mA cm(-2). High in situ stability of the porous PBI membrane was confirmed by about 50 cycles of continuous charge and discharge operation of the battery. (C) 2016 Elsevier B.V. All rights reserved.