Vacuum distillation experiments were conducted for tin-antimony alloy (Sn-Sb-alloy) under the system pressure of 5 Pa. The content of Sb (mole fraction) in crude Sn, viz., x(sb) was reduced from 0.5000 to 0.0619 in a single stage distillation process under the condition of residual pressure of 5-10 Pa, distillation temperature of 1373 K and distillation time of 60 min. The activity coefficients of components of Sn Sb alloy were calculated by using the molecular interaction volume model (MIVM), and the calculated average relative deviation and the average standard deviation were +/- 0.00039 and +/- 0.173%, respectively for both Sn and Sb. The vapor liquid equilibrium (VLE) phase diagrams, including the temperature composition (T-x) and pressure-composition (p-x) diagrams of Sn Sb alloy in vacuum distillation were calculated based on VLE theory and the MIVM. A reasonable agreement between the calculated results and the experimental data indicates that VLE phase diagrams obtained by this method are reliable. The VLE phase diagrams of alloys will provide an effective and convenient way for the designing of the process parameters of industrial production of vacuum metallurgy, and for the prediction of the needed product component dependence of temperature and pressure during the process of vacuum distillation. (C) 2016 Elsevier B.V. All rights reserved.