Vulcanization accelerant N-cyclohexyl-2-benzothiazole sulfenamide (CZ) was used as a surface modifier and chemically grafted on the surface of halloysite nanotubes (HNTs) to obtain CZ-functionalized HNTs (HNTs-s-CZ). It was found that HNTs-s-CZ could be homogeneously dispersed into styrene-butadiene rubber (SBR). The grafted CZ molecules, exactly located at the filler-rubber interface, reduced the activation energy of vulcanization of SBR/HNTs-s-CZ compounds. Besides, the density of chain segments introduced by the interfacial phase of SBR/HNTs-s-CZ nanocomposites was higher than the other nanocomposites with silane-modified HNTs (m-HNTs) or pristine HNTs, manifesting an indication of enhanced filler-rubber interfacial interaction in SBR/HNTs-s-CZ nanocomposites. Consequently, SBR/HNTs-s-CZ nanocomposites showed excellent mechanical properties. The tensile strength could be enhanced by as much as 38.6% and 102.5% compared to those of SBR/m-HNTs and SBR/HNTs nanocomposites, respectively, though containing equivalent accelerant component. The value of this work lies in the fact that apparent properties improvement of elastomer composites has been achieved by the incorporation of vulcanization accelerant-functionalized HNTs, which may be fruitful for the rational design of filler surface treatment and offer new scientific and technological opportunities for the preparation of high performance elastomer composites. (C) 2016 Published by Elsevier B.V.