MCM-41 ordered mesoporous silica was prepared, aminosilanized and grafted with polyacrylamide (PAAM) through in situ radical photopolymerization process. The resulting composite, denoted PAAM-NH2-MCM-41, the calcined and silanized reference MCM-41s were characterized by Fourier transform infrared spectroscopy (FTIR), X-ray diffraction (XRD), thermogravimetric analysis (TGA), X-ray photoelectron spectroscopy (XPS), transmission electron microscopy (TEM), scanning electron microscopy (SEM) and N-2 physisorption at 77 K. These complementary techniques brought strong supporting evidence for the silanization process followed by PAAM grafting. The surface composition was found to be PAAM-rich as judged by XPS. The composite was then employed for the uptake of Hg(II) from aqueous solutions. Adsorption was monitored versus pH, time, and temperature. The maximum adsorption capacity at 25 degrees C and pH 5.2 was 177 mg g(-1). Kinetically, the equilibrium was reached within 60 min for a 100 mgL(-1) mercury solution. The adsorption of Hg(II) on PAAM-NH2-MCM-41 composites followed second order kinetics. Thermodynamic parameters suggested that the favorable adsorption process is exothermic in nature and the adsorption is ascribed to a decrease in the degree of freedom of adsorbed ions which results in the entropy change. This work conclusively shows that mesoporous silica-polymer hybrid metal ion adsorbents (with robust silica-polymer interface) can be prepared in a simple way by in situ radical photopolymerization in the presence of aminosilanized silica acting as a support and a macro-hydrogen donor simultaneously. (C) 2016 Elsevier B.V. All rights reserved.