SiC-coated carbon fibers are prepared at room temperature with different radio-frequency magnetron sputtering powers. Results show that the coated carbon fibers have uniform, continuous, and flawless surfaces. The mean strengths of the coated carbon fibers with different sputtering powers are not influenced by other factors. Filament strength of SiC-coated carbon fibers increases by approximately 2% compared with that of uncoated carbon fibers at a sputtering power of <200 W. The filament strengths of the coated fibers increase by 9.3% and 12% at sputtering powers of 250 and 300 W, respectively. However, the mean strength of the SiC-coated carbon fibers decreased by 8% at a sputtering power of 400 W. (C) 2016 Elsevier B.V. All rights reserved.