Transparent and conductive ZnO:Al and In2O3: Sn thin films with 0.3 mu m thickness have been prepared by sputtering and subsequently annealed at temperatures ranging from 250 to 450 degrees C in N-2, 5% H-2/N-2 and air atmospheres. These samples combine high transparency (>85%) in the visible range with high electrical conductivity (>10(3) Omega(-1) cm(-1)) and plasmonic absorption in the near-infrared region, which is found sensitive to the heating temperature and environment. Such sensitivity has been related to oxidation state changes observed by X-ray photoelectron spectroscopy in the respective Zn-O and In-O bonds, since this modifies intrinsic doping by annihilation or creation of donor oxygen vacancies. The infrared plasmonic characteristics (plasma and damping energies) along with the ultraviolet absorption onset (band-gap energy) have been analyzed as a function of the carrier concentration and mobility determined by Hall-effect measurements. Assuming analogous non-parabolicity factors for the conduction band of both materials, the experimental results are consistent with lower permittivity values for ZnO: Al than for In2O3:Sn samples. (C) 2015 Elsevier B.V. All rights reserved.