We have electrochemically synthesized 3D-porous micro-nano Ni/Ni(OH)(2) hierarchical nanocomposites with improved supercapacitive performance. Firstly, the 3D-porous micro-nano Ni/Zn hierarchical nanoplatelets were constructed in a two-step gas bubble dynamic template deposition method as a scaffold with the open porous structure and extra high surface area for the subsequent electrodeposition of Ni(OH)(2) nanostructures. Then the zinc were removed from the prepared 3D Ni/Zn/Ni(OH)(2) nanocomposite via performing an etching process. The resulted 3D-porous micro-nano Ni/Ni(OH)2 hierarchical nanocomposites showed a high areal capacitance of 2.18 F cm(-2) (2400 F g(-1)) at the current density of 1.12 mA cm(-2) (1.25 A g(-1)) which is so higher than the measured amount for the prepared 3D-Ni/Ni (OH)(2) nanocomposites by directly deposition of nickel hydroxide on the synthesized 3D nickel foam. In addition, the prepared nanocomposite films exhibit the great cycling stability. The capacitance retention was about 100.012% after performing 1000 charge-discharge cycles, and decreases only about 1.3% after the 2000th cycle. (C) 2016 Elsevier B.V. All rights reserved.