TiO2-doped ZrO2 (hereafter denoted as TDZ) nanofiltration (NF) membranes with stable tetragonal phases are efficiently fabricated via a modified colloidal sol-gel process using a mixture of Zr-inorganic salts and Ti-alkoxides. Nanometer-sized TiO2-ZrO2 (hereafter denoted as TZ) colloidal sols with an average hydrodynamic diameter of similar to 2 nm are synthesized, showing good stability and reproducibility. The resulting TDZ materials are characterized by XRD, TEM, XPS, CA, mapping and nitrogen sorption. It is shown that the incorporation of Ti4+ restrains the t -> m phase transition, decreases the tetragonal crystallite size, enhances the hydrophilicity, increases the specific surface area and narrows the pore size distribution. Furthermore, these changes are promising for fabricating high performance NF membranes. The as-prepared TDZ NF membranes exhibit high performances with a low MWCO of similar to 500 Da and a high pure water permeability of 35 similar to 40 L m(-2) h(-1) bar(-1), as well as desired retention rates of 99.6% for Co2+, 99.2% for Sr2+ and 75.5% for Cs+, in simulative radioactive waste water treatment. (C) 2016 Elsevier B.V. All rights reserved.